We utilize a very sensitive electron paramagnetic resonance technique called spin-dependent recombination to observe and identify defect centers generated by modest negative bias and moderately elevated temperatures in fully processed p-channel metal-oxide-silicon field-effect transistors.... (Read more)

Interfacial defect structures of NO-nitride oxide on Si(100) were characterized by electron spin resonance spectroscopy. We confirmed that the effective g values of the P_b1 center are affected by interfacial nitridation even at a small nitrogen concentration of 5 at. %, while those of the P_b0 center proved to be unchanged. We observed that the shifted P_b1 line appeared gradually with interfacial nitrogen concentration, which suggests that the nitrogen-induced modified structure substitutes for the original P_b1 structure. Angular variations of the shifted P_b1 lines were also significantly different from those of pure oxide. Based on our analysis, we attributed the g value shift of the P_b1 center to dangling bond tilting, caused by the displacement of nearest-neighbor Si atoms. (Read more)

Interface defects generated by negative-bias temperature stress (NBTS) in an ultrathin plasma- nitrided SiON/Si(100) system were characterized by using D₂ annealing, conductance-frequency measurements, and electron-spin resonance measurements. D₂ annealing was shown to lower... (Read more)

The electronic properties of the (100) Si/SiO₂ interfacial defect called P_b1 are quite controversial. We present electron spin resonance measurements that demonstrate: (1) that the P_b1 defects have levels in the silicon band gap, (2) that... (Read more)